Title: Physical properties of extrudates containing distillers grains extruded in a twin screw extruder

Author
item CHEVANAN, NEHRU - SOUTH DAKOTA STATE UNIV
item Rosentrater, Kurt
item MUTHUKUMARAPPAN, K - SOUTH DAKOTA STATE UNIV

Submitted to: Meeting Proceedings
Publication Type: Proceedings
Publication Acceptance Date: 5/30/2007
Publication Date: 6/20/2007
Citation: Chevanan, N., Rosentrater, K.A., Muthukumarappan, K. 2007. Physical properties of extrudates containing distillers grains extruded in a twin screw extruder. 2007 ASABE Annual International Meeting, Minneapolis MN, June 17-20, 2007. Available online: www.asabe.org.

Interpretive Summary:

Technical Abstract: Extrusion trials were conducted with varying levels of distillers dried grains with solubles (DDGS) along with soy flour, corn flour, fish meal, vitamin mix, mineral mix and net protein content adjusted to 28% using a Wenger TX-52 twin screw extruder. The properties of extrudates obtained with experiments conducted using a full factorial design with 3 levels of DDGS content, 2 levels of moisture content, and 2 levels of screw speed were studied. Increasing the DDGS content from 20% to 60%, resulted in a 36.7% decrease in the radial expansion, leading to a 159% and 61.4% increase in the unit density and bulk density of the extrudates, respectively. Increasing the DDGS content resulted in a significant increase in the water absorption index (WAI), but a significant decrease in the water solubility index (WSI) of the extrudates. Changing the screw speed and moisture content had no significant effect on the radial expansion ratio, but resulted in a significant difference in the bulk density of the extrudates, which may be due to the occurrence of longitudinal expansion. Even though changing the moisture content and screw speed had no significant effect on the WSI of the extrudates, significant differences in the WAI of the extrudates were observed. Color changes in the extrudates were mostly due to color changes in the ingredient components, while moisture content and screw speed had the least effect on the color of the extrudates. Overall, it was determined that DDGS could be included at a rate of up to 60% using twin screw extrusion, and that viable pelleted floating feeds can be produced.